Effects of Processing Parameters on the Structure and Mechanical Property of PVDF/BN Nanofiber Yarns

The increasing demand for light and comfort smart wearable devices has promoted the cross-integration of textile technology with nanomaterials and nanotechnology. As a potential candidate with excellent piezoelectricity, PVDF has been processed into different forms used for flexible sensors but shows limited practicality due to their discomfort and stiffness from non-yarn level. In this study, PVDF/BN nanofiber yarns (NFYs) were successfully fabricated via conjugated electrospinning. The effects of BN concentration, stretching temperature, and stretching ratio on the structural morphology and mechanical performance of the NFYs were systematically investigated. The results show that under the stretching temperature of 140 °C and stretching ratios of 3.5, smooth 1% PVDF/BN NFYs with highly oriented inner nanofibers can be successfully fabricated, and the breaking strength and elongation of composite NFYs reached 129.5 ± 8.1 MPa and 22.4 ± 3.8%, respectively, 667% higher than the breaking strength of pure PVDF nanoyarns. Hence, with the selection of appropriate nanofiller amounts and optimized post-treatment process, the structure and mechanical property of PVDF NFYs can be significantly improved, and this study provides an effective strategy to fabricate high-performance nanoyarns, which is favorable to potential applications in wearable electronic devices and flexible piezoelectric sensors.