Mechanical Properties of Fully Recyclable 3D-Printable Materials Used for Application in Patient-Specific Devices in...

The exponential growth of plastic production in the healthcare sector and the limited capacity of conventional recycling systems have created a global environmental challenge. Latest 3D printing technologies have the potential to solve this problem by enabling on-demand, localized manufacturing. This study aimed to investigate the mechanical properties of 3D-printed ABS composites with Bi₂O₃ fillers after multiple recycling and irradiation cycles to assess their suitability for creating robust, reusable supporting devices for radiotherapy. Filaments of PLA, ABS, and ABS composites enriched with 5 wt% and 10 wt% Bi₂O₃ were extruded, repeatedly recycled through shredding and re-extrusion up to ten times and irradiated to 70 Gy using a 6 MeV photon beam to simulate clinical radiotherapy conditions. In contrast to PLA, ABS demonstrated better recyclability; however, after ten recycling cycles, its tensile strength declined from 25.1 MPa to 20.9 MPa, and its Young's modulus decreased from 2503.5 MPa to 1410.4 MPa. Incorporation of 5 wt% Bi₂O₃ into ABS significantly improved recyclability and mechanical retention. After ten recycling rounds, an ABS composite containing 5 wt% Bi₂O₃ retained tensile strength of 22.2 MPa, modulus of 1553.9 MPa, and strain at break of 14.4%. In contrast, the composite enforced with 10 wt% Bi₂O₃ showed slightly lower performance, likely due to filler agglomeration. Under irradiation, the ABS-5 wt% Bi₂O₃ composite exhibited minimal additional degradation, maintaining mechanical integrity superior to other materials. These results indicate that ABS-5 wt% Bi₂O₃ is a promising, recyclable material for durable, patient-specific devices in radiotherapy, supporting sustainability in medical manufacturing.