Preparation of Barium Europium Phosphate and Its Performance in Acrylic Resin Anti-Corrosion Coating

Acrylic resin is a polymer with strong crosslinking density and strength, and it is commonly used as a matrix in water-based coatings. Barium europium phosphate (Ba₃Eu(PO₄)₃) is a novel functional filler that is expected to provide anti-corrosive effects to coatings. In this study, Ba₃Eu(PO₄)₃ was prepared by the high-temperature solid-phase method and applied to acrylic anti-corrosion coatings. The influence of the molar ratio of reactants on Ba₃Eu(PO₄)₃ purity was studied. The anti-corrosion performance of the coating was investigated. It was found that, when BaCO₃:Eu₂O₃:(NH₄)H₂PO₄ = 3:0.5:3 and the reaction was carried out at 950 °C for 1000 min, high-purity Ba₃Eu(PO₄)₃ can be obtained, according to XRD and EDS tests. SEM shows that Ba₃Eu(PO₄)₃ has good crystal morphology and a porous morphology. TEM revealed that its structure was intact. When Ba₃Eu(PO₄)₃ was added to a relative resin content of 5 wt%, the anti-corrosion performance of the coating was the best after 168 h, with the lowest Tafel current density of 9.616 μA/cm² and the largest capacitance arc curvature radius. The salt spray resistance test showed that the corrosion resistance of the 5 wt% Ba₃Eu(PO₄)₃ coating was also the best, which is consistent with the results of the electrochemical test. Ba₃Eu(PO₄)₃ as a pigment and filler can effectively improve the anti-corrosion performance of water-based industrial coatings.