Tailored Magnetic Fe₃O₄-Based Core-Shell Nanoparticles Coated with TiO₂ and SiO₂ via Co-Precipitation:...

Background/Objectives: Magnetic nanoparticles, particularly iron oxide-based materials, such as magnetite (Fe₃O₄), have gained significant attention as contrast agents in medical imaging This study aimsto syntheze and characterize Fe₃O₄-based core-shell nanostructures, including Fe₃O₄@TiO₂ and Fe₃O₄@SiO₂, and to evaluate their potential as tunable contrast agents for diagnostic imaging. Methods: Fe₃O₄, Fe₃O₄@TiO₂, and Fe₃O₄@SiO₂ nanoparticles were synthesized via co-precipitation at varying temperatures from iron salt precursors. Fourier transform infrared spectroscopy (FTIR) was used to confirm the presence of Fe-O bonds, while X-ray diffraction (XRD) was employed to determine the crystalline phases and estimate average crystallite sizes. Morphological analysis and particle size distribution were assessed by scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM-EDX) and transmission electron microscopy (TEM). Magnetic properties were investigated using vibrating sample magnetometry (VSM). Results: FTIR spectra exhibited characteristic Fe-O vibrations at 543 cm^-1 and 555 cm^-1, indicating the formation of magnetite. XRD patterns confirmed a dominant cubic magnetite phase, with the presence of rutile TiO₂ and stishovite SiO₂ in the coated samples. The average crystallite sizes ranged from 24 to 95 nm. SEM and TEM analyses revealed particle sizes between 5 and 150 nm with well-defined core-shell morphologies. VSM measurements showed saturation magnetization (Ms) values ranging from 40 to 70 emu/g, depending on the synthesis temperature and shell composition. The highest Ms value was obtained for uncoated Fe₃O₄ synthesized at 94 °C. Conclusions: The synthesized Fe₃O₄-based core-shell nanomaterials exhibit desirable structural, morphological, and magnetic properties for use as contrast agents. Their tunable magnetic response and nanoscale dimensions make them promising candidates for advanced diagnostic imaging applications.