Mechanical Properties and Cutting Performance of Si₃N₄/Sc₂W₃O₁₂ Composite Ceramic Tools Materials

To address the poor thermal shock resistance and high brittleness of traditional ceramic tools, a novel Si₃N₄/Sc₂W₃O₁₂ (SNS) composite ceramic material was developed via in situ synthesis using WO₃ and Sc₂O₃ as precursors and consolidated by spark plasma sintering. Sc₂W₃O₁₂ with negative thermal expansion was introduced to compensate for matrix shrinkage and modulate interfacial stress. The effects of varying Sc₂W₃O₁₂ content on thermal expansion, residual stress, microstructure, and mechanical properties were systematically investigated. Among the compositions, SNS3 (12 wt.% Sc₂W₃O₁₂) exhibited the best overall performance: relative density of 98.8 ± 0.2%, flexural strength of 712.4 ± 30 MPa, fracture toughness of 7.5 ± 0.3 MPa·m^1/2, Vickers hardness of 16.3 ± 0.3 GPa, and an average thermal expansion coefficient of 2.81 × 10^-6·K^-1. The formation of a spherical chain-like Sc-W-O phase at the grain boundaries created a "hard core-soft shell" interface that enhanced crack resistance and stress buffering. Cutting tests showed that the SNS3 tool reduced workpiece surface roughness by 32.91% and achieved a cutting distance of 9500 m. These results validate the potential of this novel multiphase ceramic system as a promising candidate for high-performance and thermally stable ceramic cutting tools.