Fracture Behaviour of Basalt Fibre-Reinforced Lightweight Geopolymer Concrete: A Multidimensional Analysis

This study introduced basalt fibres as a reinforcing material and employed notched beam three-point bending tests combined with digital image correlation (DIC) technology to comprehensively evaluate key fracture parameters-namely, initial fracture toughness, unstable fracture toughness, fracture energy, and ductility index-of expanded polystyrene (EPS)-based geopolymer concrete with different mix proportions. The results demonstrate that the optimal fracture performance was achieved when the basalt fibre volume content was 0.4% and the EPS content was 20%, resulting in respective increases of 12.07%, 28.73%, 98.92%, and 111.27% in the above parameters. To investigate the toughening mechanisms, scanning electron microscopy was used to observe the fibre-matrix interfacial bonding and crack morphology, while X-ray micro-computed tomography enabled detailed three-dimensional visualisation of internal porosity and crack development, confirming the crack-bridging and energy-dissipating roles of basalt fibres. Furthermore, the crack propagation process was simulated using the extended finite element method, and the evolution of fracture-related parameters was quantitatively analysed using a linear superposition progressive assumption. A simplified predictive model was proposed to estimate fracture toughness and fracture energy based on the initial cracking load, peak load, and compressive strength. The findings provide theoretical support and practical guidance for the engineering application of basalt fibre-reinforced EPS-based geopolymer lightweight concrete.