Influence of Heat Treatment Parameters on Microhardness of Aluminium Alloy EN AW 7075 Foams and Bulk Material

Aluminium alloy foams have been widely used due to their excellent strength-to-weight ratio, low density, and outstanding properties such as high energy absorption and effective noise and heat insulation. In this study, aluminium machining chips have been used for foam production as a potential recycling method. The process has involved solution heat treatment followed by artificial ageing. Researchers have been analysing the microhardness of both the foam and the bulk material, as well as examining their microstructures. The maximum microhardness value of the bulk material has been found to be 158 ± 2 HV1 at an ageing temperature of 175 ± 1 °C for 2 ± 0.02 h. For the foams, the highest microhardness of 150 ± 2 HV1 has been achieved after ageing at 150 ± 1 °C for 9 ± 0.02 h. Experimental planning has been carried out using Design Expert software. The optimisation process has identified 150 ± 1 °C for 2 ± 0.02 h as the optimum condition for artificial ageing.