Microstructural, Mechanical, and Thermal Properties of Textured Si₃N₄/BN Composite Ceramics Prepared Using Two-Step...

Textured Si₃N₄/BN composite ceramics were successfully fabricated using two-step sintering, combining pseudo-hot isostatic pressing (PHIP) and gas pressure sintering. The grain size of h-BN platelets had a significant influence on densification and mechanical and thermal properties. With an increase in h-BN grain size, the volume density of the composite ceramics gradually decreased, while flexural strength gradually increased. Meanwhile, larger h-BN platelets were more likely to trigger toughening mechanisms like large-angle deflection and greatly increase fracture toughness. Through proper selection of h-BN grain size, textured ceramics, with the addition of h-BN platelets of 1-2 μm, showed high thermal conductivity (∼92 W∙m^-1∙K^-1) and reliable mechanical properties (∼540 MPa, ∼7.5 MPa∙m^1/2, ∼11.1 GPa). Therefore, texture control is an effective means of improving the overall performance of ceramic materials. Novel textured composite ceramics thus have great potential in large-scale fabrication and directional heat dissipation applications.