Evaluation of Printability, Color Difference, Translucency, and Surface Roughness over Time in a 3D-Printed...

Recent evidence suggests that nano-TiO₂ particles improve antimicrobial and physical properties when incorporated into dental prosthetic materials. However, there exists a paucity of information regarding their impact on material properties when the prosthetic materials are 3D-printed over time. The purpose of this study was to evaluate the time-dependent printability and surface property changes occurring in a 3D-printed denture base resin containing nano-titanium dioxide (TiO₂) particles. A 0.4 wt% concentration of 30 nm rutile TiO₂ nanoparticles was ultrasonically dispersed into a denture base resin. Disks were printed weekly using a Form 2 SLA printer until printing failed. Printability, surface roughness (R_a), color difference (ΔE_ab), and translucency parameters were measured across timepoints. Surface roughness was assessed via profilometry, while color and translucency were evaluated using a spectrophotometer under standardized conditions. Print failure occurred at week 8, beyond which the resin could no longer reliably produce full specimens. R_a roughness decreased from 3.83 µm to 0.48 µm, which denoted a significant time-dependent decrease (ρ = -0.733, p = 0.016). Color difference with the unmodified control declined from 26.32 to 17.13 ΔE_ab units (ρ = -0.976, p < 0.001). All printed samples exceeded the clinically acceptable thresholds for both R_a (0.2 µm) and ΔE_ab (<3.7). Although the printability of the resin-TiO2 mixture was maintained for 7 weeks, mixture homogeneity declined over time. TiO₂ additions to a denture polymer produced significant changes in surface roughness and color that were not clinically acceptable. Results from this study illustrate the time dependence required for retaining surface properties in 3D-printed dentures containing nano-TiO₂.