FTIR Detection of Ce³⁺ Sites on Shape-Controlled Ceria Nanoparticles Using Adsorbed ¹⁵N₂ as a Probe Molecule

Ceria is an important redox catalyst due to the facile Ce³⁺/Ce⁴⁺ switching at its surface. Therefore, in situ determination of the oxidation state of surface cerium cations is of significant interest. Infrared spectroscopy of probe molecules such as CO holds great potential for this purpose. However, the ability of CO to reduce Ce⁴⁺ cations is an important drawback as it alters the initial cerium speciation. Dinitrogen (N₂), due to its chemical inertness, presents an attractive alternative. We recently demonstrated that low-temperature ¹⁵N₂ adsorption on stoichiometric ceria leads to the formation of complexes with Ce⁴⁺ cations on the (110) and (100) planes (bands at 2257 and 2252 cm^-1, respectively), while the (111) plane is inert. Here, we report results on the low-temperature ¹⁵N₂ adsorption on reduced ceria nanoshapes (cubes, polyhedra, and rods). A main band at 2255 cm^-1, with a weak shoulder at 2254 cm^-1, was observed. We attributed these bands to ¹⁵N₂ adsorbed on Ce³⁺ sites located on edges and corners as well as on {100} facets. In conclusion, ¹⁵N₂ adsorbs on the most acidic surface Ce³⁺ sites and enables their distinction from Ce⁴⁺ cations.