The Influence of Print Orientation and Discontinuous Carbon Fiber Content on the Tensile Properties of Selective...

Discontinuous fibers are commonly added to matrix materials in additive manufacturing to enhance properties, but such benefits may be constrained by print and fiber orientation. The additive processes of forming rasters and layers in powder bed fusion inherently cause anisotropy in printed parts. Many print parameters, such as laser, temperature, and hatch pattern, influence the anisotropy of tensile properties. This study characterizes fiber orientation attributed to recoating non-encapsulated fibers and the resulting anisotropic tensile properties. Tensile and fracture properties of polyamide 12 reinforced with 0%, 2.5%, 5%, and 10% discontinuous carbon fibers by volume were characterized in two primary print/tensile loading orientations: tensile loading parallel to the recoater ("horizontal specimens") and tensile load along the build axis ("vertical specimens"). Density and fractographic analysis indicate a homogeneous mixture with low porosity and primary fiber orientation along the recoating direction for both print orientations. Neat specimens (zero fiber) loaded in either direction have similar tensile properties. However, fiber-reinforced vertical specimens have significantly reduced consistency and tensile strength as fiber content increased, while the opposite is true for horizontal specimens. These datasets and results provide a mechanism to tune material properties and improve the functionality of selectively laser-sintered fiber-reinforced parts through print orientation selection. These datasets could be used to customize functionally graded parts with multi-material selective laser-sintering manufacturing.