The Effect of Hydroxyapatite-Coated, Reinforced, Nonabsorbable Polyfilament Suture Material on Tendon-Bone Healing
Mustafa Ozkaya1, Taha Kizilkurt1, Bengisu Kubasik2
1Department of Orthopedics and Traumatology, Istanbul University Faculty of Medicine, Istanbul, Türkiye.
Background:
Anterior cruciate ligament (ACL) injuries are prevalent among athletes and the general population, with ACL reconstruction (ACLR) being the standard treatment. However, effective tendon-bone healing (TBH) remains a challenge. Hydroxyapatite (HAp), widely used in orthopaedics and dentistry, has yet to be fully explored for its potential to enhance TBH.
Hypothesis:
HAp-coated, reinforced, nonabsorbable suture materials can act as a bioactive and osteoinductive bridge, expediting TBH after ACLR.
Study Design:
Controlled laboratory study.
Methods:
Gelatin-based solutions were used to coat suture materials with HAp, forming stable layers analyzed via scanning electron microscopy and energy-dispersive spectrum. Sixteen New Zealand rabbits underwent extra-articular TBH modeling, with the right knee as the experimental group and the left as the control. Evaluations were conducted at 6 and 12 weeks, including histomorphometry, microcomputed tomography (micro-CT) for bone formation and mineral density, and tensile testing to assess mechanical properties.
Results:
Histological analysis demonstrated significantly higher bone/fibrous interzone area ratios in the experimental group at the 6th week (1.24 ± 0.14 vs 0.45 ± 0.18; P = .011) and 12th week (2.07 ± 0.47 vs 0.74 ± 0.11; P = .013). Circumferential bone formation at the 6th week was markedly greater in the experimental group (89.17% ± 5.97% vs 29.66% ± 10.05%; P = .012). Micro-CT showed increased bone mineral density (2.09 ± 0.41 vs 1.35 ± 0.36; P = .037) and reduced bone tunnel circumference at the 12th week. Biomechanical tests indicated greater stiffness (4.22 ± 1.33 vs 3.18 ± 0.76; P = .044), with no significant differences in failure load or displacement at the 12th week.
Conclusion:
HAp-coated sutures significantly improved TBH (particularly histological results at the 6th week), enhancing bone integration and mechanical properties in the extra-articular TBH model.
Clinical Relevance:
The use of HAp-coated nonabsorbable polyfilament sutures may enhance TBH. Early histological evaluations indicated a positive effect on TBH, which was further corroborated by radiological and biomechanical improvements. These findings warrant further clinical investigation to explore potential applications.
Related Concept Videos
01:23Bone as Supporting Connective Tissue
Bone Matrix
Bone, or osseous tissue, is a connective tissue that has a large amount of two different types of matrix material. The organic matrix is similar to the matrix material found in other connective tissues, including some amount of collagen and elastic fibers. This gives strength and flexibility to the tissue. The inorganic matrix consists of mineral salts— mostly calcium salts— that give the...
01:19The Effect of Aging on Tissues
01:18The Bone Matrix
01:29Bone Disorders
Bone deposition is also affected by the levels of sex hormones like estrogen and testosterone that promote osteoblast activity and bone matrix synthesis. When the level of these hormones decreases due to aging, it causes a reduction in bone deposition. As a result, bone resorption by osteoclasts...
01:31Essential Minerals for Bone Health
Calcium and Phosphorus
Calcium is a critical component of bones, especially in the form of calcium phosphate and calcium carbonate. Since the body cannot make calcium, it must be obtained from the diet. However, calcium cannot be absorbed from the small intestine without...
01:24Bone Formation by Endochondral Ossification