Controlling Sodium Titanate Crystal Size to Improve Wettability and Early Osseointegration of Titanium Implants:...

The thermo-chemical treatment of dental implants leads to the formation of sodium titanate crystals on their surface. When in contact with blood, these crystals dissolve and trigger an ionic exchange cascade, resulting in the formation of a calcium apatite layer. This study, carried out both in vitro and in an animal model, aimed to determine whether the cooling rate of the treatment affects the size of the deposited crystals, and whether this in turn influences wettability and early bone-to-implant contact (BIC). A total of 50 dental implants and 50 titanium discs were treated using four different cooling rates, along with a control group. Crystal size was analyzed on implant surfaces using scanning electron microscopy, and wettability was assessed on titanium discs using a goniometer. Finally, the implants were placed in the tibiae of 13 rabbits, and histological analysis was performed after three weeks to compare BIC among groups. Results suggest that a cooling rate of 75 °C/h produces smaller sodium titanate crystals, which are associated with significantly improved surface wettability and a higher percentage of bone-to-implant contact after 3 weeks of healing (p < 0.05).