Chitosan/halloysite clay mixture for preservation of waterlogged archaeological woods

M R Caruso1, G D'Agostino2, G Cavallaro1

  • 1Department of Physics and Chemistry "Emilio Segrè", Università degli Studi di Palermo, Viale delle Scienze, Ed. 17 "Stanislao Cannizzaro", 90128 Palermo, Italy.

International Journal of Biological Macromolecules
|August 27, 2025
PubMed

Keywords:
Archaeological woodChitosanConservationDMAHalloysite clay nanotubes

More Related Videos

Determination of the Settling Rate of Clay/Cyanobacterial Floccules06:00

Determination of the Settling Rate of Clay/Cyanobacterial Floccules

Published on: June 11, 2018

7.0K
Preparation of Expanded Chitin Foams and their Use in the Removal of Aqueous Copper06:36

Preparation of Expanded Chitin Foams and their Use in the Removal of Aqueous Copper

Published on: February 27, 2021

3.8K

Related Concept Videos

Seasoning of Wood01:15

Seasoning of Wood

Seasoning of wood is a crucial process aimed at reducing and stabilizing the moisture content within the wood to prevent future shrinkage, structural damage, or aesthetic issues once the wood is used in construction. Wood naturally swells when it absorbs moisture and contracts as it dries.
Achieving equilibrium moisture content is the goal of seasoning; this is the point where the wood's moisture content stabilizes to align with the moisture levels of the surrounding environment. Proper...
Deleterious Substances in Aggregate01:25

Deleterious Substances in Aggregate

Deleterious substances in aggregates can be detrimental to the quality and durability of concrete. These substances include organic impurities like loam, which interfere with cement hydration and are usually present in the sand. These prevent a good bond between aggregate and cement paste. Organic impurities can be detected using the colorimetric test, where the darkness of a solution after agitation indicates the level of organic content.
Another type of impurity is clay and fine material that...
Quality of Water01:19

Quality of Water

In concrete preparation, the quality of water is paramount as it affects the strength and durability of the concrete. Potable water is usually preferred; however, it must not have excessive sodium or potassium to prevent compromising the concrete's integrity. Water quality is typically evaluated based on impurities such as dissolved solids, chlorides, and sulfates, and its pH value is ideally between 6 and 8. Even slightly acidic natural water may be acceptable unless it contains harmful...
Testing Water Quality01:14

Testing Water Quality

When the quality of water for concrete preparation is uncertain, its impact on the setting time of cement and compressive strength of mortar is assessed by comparison with de-ionized or distilled water benchmarks. American Society for Testing and Materials (ASTM) C1602 requires the setting times to be within 90 minutes of the control, British Standard (BS) 3146:1980 allows a 30-minute variance in the initial setting, while British Standards European Norm (BS EN) 1008 specifies initial setting...
Effect of Sea Water on Concrete01:22

Effect of Sea Water on Concrete

Concrete exposed to seawater can undergo degradation like the dissolution of ettringite and gypsum, increasing the material's porosity and decreasing its strength. In contrast, the crystallization of salts within the concrete's pores can cause expansion, particularly above the waterline where evaporation occurs. Nonetheless, this expansion only happens when seawater, enabled by the concrete's permeability, manages to infiltrate the structure.
Concrete in areas between tide marks, which undergo...
Acid Attack on Concrete01:21

Acid Attack on Concrete

When acids come into contact with concrete, they initiate a chemical reaction that dissolves the hydrated cement paste. This process leads to softening and structural weakening of the concrete. This issue is commonly observed in environments such as chimneys, sewers, and industrial settings. The severity of the damage increases as the pH of the water interacting with the concrete drops below 6.5. In particular, a pH under 4.5 can cause significant concrete damage.
The rate at which hydrogen...