Tribological Properties of Diamond/Diamond-like Carbon (DLC) Composite Coating in a Dry Environment

In this study, a diamond/diamond-like carbon (DLC) composite coating was designed and fabricated utilizing a combination of chemical vapor deposition (CVD) and magnetron-sputtering-assisted ion beam deposition. This was designed to cope with severe problems such as high wear due to insufficient lubrication under dry sliding conditions with a single diamond. The tribological properties of the fabricated coatings under dry conditions were comparatively evaluated. The results demonstrate that the diamond/DLC composite coatings significantly enhance the tribological performance relative to their single-layer diamond counterparts. Specifically, a 33.73% reduction in the average friction coefficient and a 39.55% decrease in the average wear rate were observed with the MCD (microcrystalline diamond/DLC coating. Similarly, a 16.85% reduction in the average friction coefficient and a 9.69% decrease in the average wear rate were observed with the UNCD (ultrananocrystalline diamond)/DLC coating. Analysis of the worn track morphology and structure elucidated the underlying friction mechanism. It is proposed that the DLC top layer reduces the surface roughness of the underlying diamond coating and mitigates abrasive wear in the dry environment. Furthermore, the presence of the DLC film promotes graphitization via phase transition during sliding, which enhances lubricity and facilitates the establishment of a smooth friction interface.