Fabrication of Cu-Al-Mn-Ti Shape Memory Alloys via Selective Laser Melting and Its Nano-Precipitation Strengthening

A Cu-11.85Al-3.2Mn-0.1Ti shape memory alloy (SMA) with excellent superelasticity and shape memory effect was successfully fabricated via selective laser melting (SLM). Increasing the energy density enhanced grain refinement, achieving a 90% refinement rate compared to cast alloy, with an average width of ~0.15 µm. Refined martensite lowered transformation temperatures and increased thermal hysteresis. Nanoscale Cu₂TiAl phases precipitated densely within the matrix, forming a dual strengthening network combining precipitation hardening and dislocation hardening. This mechanism yielded a room-temperature tensile strength of 829.07 MPa, with 6.38% fracture strain. At 200 °C, strength increased to 883.68 MPa, with 12.26% strain. The maximum tensile strength represents a nearly 30% improvement on existing laser-melted quaternary Cu-based SMAs.