Experimental Study on the Application of Limestone Mine Dust Filter Slag as Concrete Admixture

With rapid industrialization, large quantities of industrial solid waste are generated annually. In Panzhihua, China, approximately 300,000 tons of limestone mine dust filter residue (LMDFR) is produced. This study investigates the properties of LMDFR and its potential as a supplementary cementitious material. LMDFR was blended with fly ash (FA) to replace 30% of cement in mortar. Tests were conducted to measure the mortar's flowability and its compressive and flexural strengths after 7 and 28 days of curing, and XRD, SEM, TG, and DSC analyses were conducted on 28-day specimens. LMDFR primarily comprises ≥95% CaCO₃, with a specific surface area of ~1.3 m²/g and density of 2.694 g/cm³. Mortar flowability increased with LMDFR content, reaching 112.83% when used alone. Flexural strength was largely unaffected, while the 7-day compressive strength significantly improved. However, the 28-day strength decreased when LMDFR was used alone, with a 28-day activity index of 61.10%, compared with 71.52% for FA. A 1:1 blend of LMDFR and FA improved the activity index to 83.18%. Microstructural and thermal results corroborated strength and flowability trends. In conclusion, LMDFR demonstrates promising potential as a supplementary cementitious material in concrete applications. When blended with fly ash at a 1:1 ratio, the composite admixture significantly enhances flowability and early compressive strength while maintaining adequate long-term performance. This synergistic combination not only improves the physical properties of cement mortar but also provides a sustainable solution for the large-scale utilization of industrial solid waste.