Effect of Curing Parameter on the Performance of Electric-Induced Heating-Cured Carbon Fiber-Reinforced Conductive...

Winter concrete construction is a pivotal engineering issue that needs to be addressed due to the failure of cementitious materials to hydrate under severely low temperatures. To solve the problem, the electric-induced heating curing (EIH) method was presented to prepare cement mortar (CF-CM) at an environmental temperature of -20 °C. The influence of some key parameters, including carbon fiber (CF) content (0-0.9 vol%), preparation methods, and EIH curing regimes (constant power vs. constant voltage; frequency: 30-70 Hz), on the performance of CF-CM were examined. Furthermore, the curing temperature of EIH-cured specimens were simulated based on COMSOL Multiphysics software. The results demonstrated that the electrical percolation threshold of CFs inside the specimen was 0.6 vol%. EIH curing achieved 1-day early strength equivalent to 2 days of standard curing, and increasing CF content showed little influence on the mechanical properties of CF-CM specimens. Moreover, constant-power EIH maintained stable curing temperatures (>50 °C), outperforming unstable constant voltage curing. Applied frequency (30-70 Hz) exhibited negligible impact on compressive strength, validating standard 50 Hz AC for practical application. Furthermore, the optimal EIH power density identified based on COMSOL Multiphysics software was 667 W/m², successfully maintaining specimen temperatures between 60 °C and 70 °C to enable rapid strength development under sub-zero conditions, laying a foundation for the use of COMSOL in the guidance of EIH curing regime design. This work provides a scientifically grounded and applicable solution for winter concrete construction.