Experimental and Simulation Study on Residual Stress of Pure Copper Welded Joint by Laser Shock Peening

To accurately assess the residual stress distribution on the superficial layer of the weld for a pure copper butt-welded joint after laser shock peening (LSP), a coupled model was established by integrating experimental measurements with numerical simulations. This model simulates both the tungsten inert gas (TIG) welding process of pure copper and the subsequent LSP treatment applied to the weld. On this basis, the effects of the spot overlapping rate, number of impact layers, and pulse width on the weld residual stress profile were evaluated via multi-point LSP simulations. The findings imply that LSP converts the weld's superficial residual stress from tensile to compressive, which verifies the accuracy of the simulations through the experimental data. Multi-point LSP numerical simulations demonstrate that elevating the spot overlapping rate and number of impact layers enhances the amplitude and affected depth of the surface compressive residual stress (CRS). A slight decrease in the CRS on the superficial layer of the weld was observed with an increase in pulse width. Compared with increasing the overlapping rate and pulse width, increasing the number of impact layers has a more significant strengthening effect. When the impact layer reached 3 times, the surface CRS reached -219.4 MPa, and the influence depth was 1.3 mm.