Study on the Influence and Performance of Nano SiO₂ on Solid Waste Grouting Material

As a key connection technology in prefabricated buildings, offshore wind power, and bridge engineering, the performance and environmental sustainability of grouted sleeve connections are essential for the long-term development of civil infrastructure. To address the environmental burden of conventional high-strength cement-based grouts, an eco-friendly sleeve grouting material incorporating industrial solid waste was developed. In this study, silica fume (15%) and fly ash (5%) were employed as supplementary cementitious materials, while nanosilica (NS) was introduced to enhance the material properties. Mechanical testing, microstructural characterization, and half-grouted sleeve uniaxial tensile tests were conducted to systematically evaluate the effect of NS content on grout performance. Results indicate that the incorporation of NS significantly accelerates the hydration of silica fume and fly ash. At an optimal dosage of 0.4%, the 28-day compressive strength reached 105.5 MPa, representing a 37.9% increase compared with the control group without NS. In sleeve tensile tests, specimens with NS exhibited reinforcement necking failure, and the load-displacement response closely aligned with the stress-strain behavior of the reinforcement. A linear relationship was observed between sleeve wall strain and reinforcement stress, confirming the cooperative load-bearing behavior between the grout and the sleeve. These findings provide theoretical guidance and technical support for developing high-strength, low-impact grouting materials suitable for sustainable engineering applications.