Influences of Strain Rates on Tensile and Shear Performances of CF/PP and GF/PP Thermoplastic Composites

This study aims to investigate the influences of strain rates on tensile and shear performances of carbon fiber-reinforced polypropylene (CF/PP) and glass fiber-reinforced polypropylene (GF/PP) thermoplastics. First, the differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) tests were conducted on the polypropylene to determine its melting and decomposition temperatures, identified as approximately 166 °C and 450 °C, respectively. Subsequently, CF/PP and GF/PP specimens were fabricated through the thermo-compression molding process, and subjected to the uniaxial tension and bias extension tests across six strain rates (1.7 × 10^-6 s^-1, 0.5 s^-1, 5 s^-1, 50 s^-1, 250 s^-1, and 500 s^-1). The results indicated that the tensile modulus/strength and shear modulus/strength of both CF/PP and GF/PP specimens improved with the increase in strain rates, whereas the shear failure strain exhibited a decreasing trend due to the transition of polypropylene from ductile to brittle behaviors. At 500 s^-1, CF/PP exhibited 53.08%/53.6% and 52.5%/52.4% increases in tensile/shear modulus and tensile/shear strength compared to 1.7 × 10^-6 s^-1, while GF/PP showed 54.6%/113.4% and 71.5%/92.3% improvements, respectively. Furthermore, fracture surfaces exhibited progressive roughening with increasing strain rates. The dynamic increase factor (DIF) quantitatively characterized the strain rate dependencies of elastic and strength properties, establishing an analytical model for developing rate-dependent constitutive models in future research.