Study on Electrochemical Corrosion Behavior of Plasma Sprayed Al₂O₃-3%TiO₂ Coatings Doped with CeO₂ for Long-Term...

The long-term corrosion behavior of Al₂O₃-3%TiO₂ (AT3) coatings doped with1%, 5% and 8% CeO₂ prepared by plasma spraying was studied in 5% NaCl solution. The results showed that the protective performance of CeO₂-doped coatings was significantly higher than that of undoped coatings, primarily due to the reduction in coating porosity caused by the addition of rare-earth elements. Among the doped coatings, the 5% CeO₂-doped coating exhibited the best protective performance. The addition of rare-earth oxides CeO₂ reduced the content of γ-Al₂O₃ in the coating, but when the concentration of CeO₂ increased to 8%, the Ce element was rich in the gap of the coating. Excessive CeO₂ enriched in the gaps and coexisted more with Ti, and prevented the formation of the AlTi phase, which affected the performance of the coating. Electrochemical and XPS results revealed that an appropriate amount of Ce atoms or CeO₂ particles could fill the pores of the coating. During long-term immersion, Ce (IV) was converted to Ce (III), which demonstrated that Ce atoms have high chemical activity in coatings. The thermodynamic calculation results show that more CeO₂ particles improved the adsorption of corrosive ions. It indicated that the content of doped rare-earth oxides exceeding 5% would be utilized as an active material in the corrosive process.