Microstructure and Mechanical and Corrosion Behavior of Novel High-Entropy CoCrFeNiSiV_x (x = 0.25; 0.5; 0.75; 1.0)...

In this work, a series of novel high-entropy alloys CoCrFeNiSiV_x (x = 0.25; 0.5; 0.75; 1.0) with an intermetallic compound structure was proposed. The effect of vanadium addition on the structure, as well as selected mechanical and corrosion properties, was investigated. In the case of the CoCrFeNiSiV_0.25 alloy, the structural analysis revealed the formation of a dual-phase structure consisting of Fe_1.812V_0.907Si_0.906-type and Fe₅Ni₃Si₂-type intermetallic phases. The increase in vanadium concentration results in the crystallization of one Fe_1.812V_0.907Si_0.906 intermetallic phase detected by the X-ray diffraction method. The increase in vanadium content had a beneficial influence on the corrosion resistance of CoCrFeNiSiV_x alloys in 3.5% NaCl. The CoCrFeNiSiV alloy exhibited the lowest corrosion current density of 0.17 μA/cm² and the highest corrosion potential of -0.228 V. The hardness of the alloys investigated increased with vanadium content, reaching 1006 HV for the equimolar alloy. In turn, the lowest friction coefficient of 0.63 ± 0.06 was obtained for the CoCrFeNiSiV_0.75 alloy. The abrasive, fatigue, and oxidative wear were identified as the main wear mechanisms.