Electrospun Polymeric Film in Red BF-4B Dye Degradation

This work aims to apply polymeric PBAT/PLA fibers electrospun with TiO₂ in the photodegradation of the dye Red BF-4B in an aqueous solution and the dye's subsequent reuse. Initially, the influence of the solution pH was evaluated, and the results showed more significant dye degradation at pH values below the pHpcz (7.42). Kinetic studies show that at 15 mg·L^-1, the highest percentage of degradation occurs at 600 min of reaction time; however, degradation equal to (or greater than) 65% was observed at all evaluated concentrations, with the kinetic data being well fitted by the pseudo-first-order model. Additional studies demonstrated the reuse of polymeric films for dye removal, with removal efficiencies ranging from 86.60% to 93.07% over six consecutive reuse cycles. Each cycle consisted of a 600 min removal process, simulating repeated practical applications. After the photocatalytic process, the polymeric fibers remained cylindrical, with several fractures. Diameter decreases of 31.61% and 7.95% were observed after the first and sixth cycles, respectively, with possible exposure of TiO₂. The vibrational spectra indicate changes in the bands at 1755 and 1714 cm^-1, attributed to C=O (PLA) and C-O (PBAT) stretches, respectively, suggesting a possible conformational change in the polymers. The thermal profiles showed only slight changes after the cycles. X-ray diffractograms indicate that degradation of the polymeric matrix leads to greater exposure of the embedded TiO₂ particles. The combined results from different characterization techniques provide evidence of the degradation of the polymeric material.