Phosphate Low-Melting Glasses as Synergist in Flame-Retardant Cable Sheath Composition: Performance and Mode of...

Nowadays, fiber optic cables are a strategic issue because of their importance in telecommunications. Due to the densification of optic cables and the reduction in polymeric layer thickness, the flammability of the external sheath has to be improved. Three novel flame-retardant compositions using phosphate low-melting glasses (LMGs) as aluminum trihydrate (ATH) synergist were assessed in a polyethylene-ethylene vinyl acetate (PE-EVA) matrix. It was highlighted that LMG at a 10 wt% content reduced the peak and mean value of heat release rate (HRR), respectively, to 142 and 90 kW/m² corresponding to 52% and 42% reduction compared to ATH only. Potassium phosphate LMG was shown to perform better than sodium or zinc phosphate LMG. The improvement was assigned to the formation of an expanded mineral layer at the surface of the material during combustion that acts as a thermal shield slowing down the pyrolysis rate. The structural analysis revealed that the presence of alkaline cations in glasses led to short phosphate chains that resulted in low softening point and low-viscosity liquid. It was evidenced that under heat exposure the melted glass is likely to flow between the dehydrating ATH particles, creating a cohesive layer that expands. Additionally, interactions between ATH and LMG were also evidenced. The new crystalline species may also play a role in the cohesion of the layer.