Effects of Ni Content on Energy Density, Capacity Fade and Heat Generation in Li[Ni_xMn_yCo_z]O₂/Graphite Lithium-Ion...

The demand for high energy density in mobile devices (including vehicles and small ships) is increasing. Nickel-Manganese-Cobalt (NMC) ternary, as a battery cathode material, is increasingly being applied because of its higher energy density relative to LiFePO₄ or other traditional materials. But NMC also faces challenges, such as a high degeneration rate and heat generation. So these aspects of Ni content must be clarified. In the current study, two Ni-content battery cells were tested, and the results of other composition cathode cells from the literature were compared. And three typical Ni-content batteries were simulated for searching Ni effects on performance, capacity fade and heat generation. Some findings were achieved: (1) from 0.8 Ni content, it can be seen that the specific capacity growth rate (slope) was much greater than before; (2) cathode materials that have an odd number (that does not surpass 0.7) of Ni content showed a linear capacity degradation trend, but others did not; (3) the Li concentration within material particles did not correspond to absolute stress value but stress temporal gradient; and (4) during discharge, lower Ni content made the heat peak occur earlier but lowered the absolute value; the irreversible heat increased with Ni content non-linearly, so that the higher the Ni content went up, the higher the increase rate of the irreversible heat ratio. Thus, the results of this study can guide the design and application of high energy batteries for mobile devices.