Effect of Secondary Aging Conditions on Mechanical Properties and Microstructure of AA7150 Aluminum Alloy

Al-Zn-Mg-Cu alloys are widely used as heat-treatable ultra-high-strength materials in aerospace structural applications. While conventional single-stage aging enables high strength, advanced performance demands call for precise microstructural control via multi-stage aging. In this study, we employ a combination of scanning transmission electron microscopy (STEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD) to investigate the microstructural evolution and its correlation with mechanical properties of AA7150 aluminum alloy subjected to two-step aging treatments, following a 6 h pre-aging at 120 °C. Through atomic-scale STEM imaging along the [110]_Al zone axis, we systematically characterize the precipitation behavior of GPII zones, η' phases, and equilibrium η phases both within the grains and at grain boundaries under varying secondary aging (SA) conditions. Our results reveal that increasing the SA temperature from 140 °C to 180 °C leads to coarsening and reduced number density of intragranular precipitates, while promoting the continuous and coarse precipitation of η phases along grain boundaries, accompanied by a widening of the precipitation-free zone (PFZ). Notably, SA at 160 °C induces the formation of fine, uniformly dispersed nanoscale η' precipitates in the alloy, as confirmed by XRD phase analysis. Aging at this temperature markedly enhances the mechanical properties, achieving an ultimate tensile strength (UTS) of 613 MPa and a yield strength (YS) of 598 MPa, while presenting an exceptionally broad peak-aging plateau. Owing to this feature, a moderate extension of the SA duration does not reduce strength and can further improve ductility, increasing the elongation (EL) to 14.26%. These results demonstrate a novel two-step heat-treatment strategy that simultaneously achieves ultra-high strength and excellent ductility, highlighting the critical role of advanced electron microscopy in elucidating phase-transformation pathways that inform microstructure-guided alloy design and processing.