Degradation of oxytetracycline in wastewater by catalytic ozonation with eggshell-derived calcium peroxide

Calcium peroxide (CaO₂) was successfully synthesized from calcium-rich eggshell waste through a multi-step process. First, the eggshell waste was naturally dried, ground, and calcined at varying temperatures (700, 800, or 900 °C) for 2 hours, resulting in the formation of calcium oxide (CaO). Subsequently, CaO₂ was synthesized via a precipitation method, in which CaO was mixed with hydrogen peroxide (H₂O₂) at varying concentrations (25%, 30%, or 35%). The formation of CaO₂ was initially confirmed by its characteristic yellowish appearance. The properties of the eggshell waste, CaO, and CaO₂ were characterized using X-ray diffractometry (XRD), Fourier-transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The XRD results indicated that higher calcination temperatures enhanced the crystallinity of CaO, while increasing the H₂O₂ concentration led to a reduction in the crystalline structure of CaO₂. The performance of CaO₂ as a catalyst in catalytic ozonation was evaluated for the degradation of oxytetracycline (OTC) in synthetic wastewater. Under the designated conditions (pH 7, 3 g per L CaO₂, and 60 min reaction time), OTC removal efficiency reached 100%, whereas sole ozonation achieved only 85.7%. The pseudo-first-order reaction rate constant (k _obs) for composite B (30% H₂O₂ with 1 : 1 mole ratio between CaO and H₂O₂) was 0.1152 min^-1, which was significantly higher than that of sole ozonation (k _obs = 0.0365 min^-1), demonstrating the catalytic efficiency of CaO₂.