Photocatalytic Evaluation of Fe₂O₃-TiO₂ Nanocomposites: Influence of TiO₂ Content on Their Structure and Activity

In this study, Fe₂O₃-TiO₂ nanocomposites with different TiO₂ contents (1-50%) were synthesized via a solvothermal method using pre-formed α-Fe₂O₃ nanoparticles as cores. We systematically evaluated the influence of TiO₂ loading on the nanocomposites' structural, morphological, optical, and photocatalytic properties. X-ray diffraction revealed the coexistence of hematite and anatase phases, with an increase in TiO₂ content inducing reduced crystallite size, enhanced dislocation density, and microstrain, indicating interfacial lattice distortion. Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) showed a uniform elemental distribution at low TiO₂ contents, evolving into irregular agglomerates at higher loadings. Fourier-transform infrared (FTIR) spectra indicated the suppression of Fe-O vibrations and the appearance of hydroxyl-related bands with TiO₂ enrichment. Diffuse reflectance spectroscopy (DRS) analysis confirmed the simultaneous presence of hematite (~2.0 eV) and anatase (3.2-3.35 eV) absorption edges, with a slight blue shift in the TiO₂ band gap at higher concentrations. Photocatalytic activity, assessed using methylene blue degradation under xenon lamp irradiation, demonstrated a strong dependence on the TiO₂ fraction. The composite containing 33% TiO₂ achieved the best performance, with 98% dye removal and a pseudo-first-order rate constant of 0.045 min^-1, outperforming both pure hematite and commercial P25 TiO₂. These results highlight that intermediate TiO₂ content (~33%) provides an optimal balance between structural integrity and photocatalytic efficiency, making Fe₂O₃-TiO₂ heterostructures promising candidates for water purification under simulated solar irradiation.