Microstructure, Mechanical and Tribological Properties of Cold Sprayed Fe-Based Metallic Glass Coatings

Iron-based metallic glasses are gaining increased interest due to their good glass-forming ability, high compressive strength, high corrosion resistance, catalytic properties, excellent soft magnetic properties, and relatively low cost. Cold spraying was successfully used to produce amorphous coatings from commercially available powder without any crystallization due to its high cooling rate and short processing time, minimizing thermal influences. Thick and dense amorphous coatings were obtained. The effect of a substrate on the microstructure, phase composition, microhardness, flexural strength, and wear behaviour of the coatings was investigated. The cold sprayed coatings revealed an almost complete amorphous structure and negligible porosity. The coating deposited on the steel substrate showed higher microhardness, better resistance to loose abrasive wear, and a slightly lower wear index tested in the coating and Si₃N₄ ball tribological association than that cold sprayed on an Al alloy. The force required to destroy the durability of the coating-steel substrate system estimated during three-point bending tests was also much higher. Both coatings were characterized by a comparable friction coefficient.