Study on Alkali-Activated Slag Mortar Based on Co-Modified Recycled Fine Aggregate with Nano-SiO₂ and Sodium Silicate...

The widespread use of recycled fine aggregate (RFA) is hindered by its porous and weak adhered mortar. In this study, a nano-SiO₂-sodium silicate mixed solution (NMS) was used to soak and strengthen the adhered mortar. Alkali-activated slag was adopted as the cementitious material, and the resulting treated waste liquid (RNMS) was recycled as a sodium silicate source for the alkali activator. The effects of modified RFA (MRFA) incorporation and RNMS use on the performance, economic, and environmental benefits of alkali-activated slag recycled fine aggregate mortar (AASRM) were evaluated. Compared with the control group, mortars using only MRFA showed significantly improved performance, with a 28-day compressive strength increase of 57.6% (reaching 38.3 MPa) and enhanced workability. The capillary water absorption and 90-day drying shrinkage rates decreased by 49.5% and 40.2%, respectively. Microstructural analysis revealed that NMS treatment promoted the formation of additional C-(N)-A-S-H gel, thereby densifying the surface of the RFA and strengthening the interfacial transition zone (ITZ). More importantly, using RNMS as the alkali activator source maintained the excellent performance of the AASRM mortar, with the compressive strength reaching 95.6% of that prepared with a fresh alkali activator, while effectively reducing material costs and embodied carbon. This study not only successfully applies MRFA in alkali-activated mortar systems but also provides an effective approach for the in situ recycling of treated waste liquid.