Integrated Performance and Capability Analysis of Anticorrosive Cathodic Electrodeposition Coatings: Effect of...

The presented research delivers a comprehensive evaluation of anticorrosive cathodic electrodeposition (CED) coatings through an integrated performance and process capability analysis-an approach that remains extremely limited in the literature, particularly in the context of statistically designed experiments (DoEs) applied to CED systems. This study therefore addresses a notable gap by focusing on the role of polymerization variables in determining coating quality through DoE to quantify the influence on coating thickness uniformity, adhesion integrity and impact resistance, while all other deposition parameters were rigorously controlled. Prior to coating application, all specimens were prepared and conditioned in accordance with ISO 1513:2010. Coating thickness was determined in compliance with ISO 2808:2019, adhesion was characterized by cross-cut methodology according to ISO 2409:2020 and dynamic mechanical resistance was evaluated using a falling-weight apparatus in accordance with ISO 6272-1:2011. The obtained datasets were subjected to statistical capability analysis within the PalstatCAQ environment, providing Cp, Cpk, Pp and Ppk indices in line with ISO 22514-7:2021 and IATF 16949:2016 requirements. Results evidenced non-linear dependencies of thickness formation on curing parameters, with potential capability indices (Cp > 1.8; Pp ≈ 1.4) indicating favorable process dispersion, while performance indices (Cpk < 0.5; Ppk < 0.4) revealed systematic mean shifts and deviations from normality confirmed by Shapiro-Wilk and Anderson-Darling tests. Adhesion testing demonstrated a direct correlation between curing conditions and interfacial bonding, reaching ISO Grade 0 classification. Complementary impact resistance assessments corroborated these findings, showing that insufficient curing induced extensive cracking and delamination. Furthermore, SEM-EDX analysis performed on Sample n.3 of X₂ variable confirmed the chemical integrity and multilayered structure of the CED coating.