A Study on Thin Cooling Layers Between the Cooling Channel and Cavity in the Injection Molding Process for Mold...

Weld lines in injection-molded plastics often act as structural weak points that reduce mechanical performance. Enhancing weld line strength is therefore essential to improve product reliability and service life. This study aims to develop and validate an injection mold system capable of localized cavity temperature control to strengthen weld line regions. A specialized mold with an integrated cooling layer was designed to enable rapid thermal response during molding. The Taguchi method was applied to optimize three key parameters-part thickness, melt temperature, and injection pressure-to maximize weld line flexural strength. Experiments based on an L25 orthogonal array revealed that weld line stress varied significantly across parameter combinations, with a maximum of 109.23 MPa. A subsequent validation test conducted under the optimal conditions (250 °C melt temperature, 1.5 mm part thickness, and 16 MPa injection pressure) achieved an enhanced weld line stress of 121.88 MPa, confirming the reliability of the Taguchi-based optimization. Among the factors studied, part thickness had the greatest influence, followed by injection pressure, while melt temperature had the smallest effect. These results demonstrate that combining cavity temperature control with systematic parameter optimization provides an effective strategy to enhance weld line strength in high-performance plastic components.