Evaluation of Workability and Crack Resistance of Recycled Plastic Asphalt Mixtures

To address the global plastic crisis, recycled plastics from food packaging were used as road materials by the dry method for practical application research. First, the main components of the recycled plastics were identified based on FTIR, and their thermal stability was evaluated through DSC, TG, and microscopic analysis. Then, the workability of the plastic-asphalt mixture was evaluated using the gyratory compaction indicator, void content, and compaction energy index (CEI). Finally, the effect of reused plastics on the cracking resistance of bituminous mixtures was examined with the Superpave IDT test. The results indicate that recycled plastics from food packaging are polyolefin composite materials, primarily consisting of Low-Density Polyethylene (LDPE), Linear Low-Density Polyethylene (LLDPE), High-Density Polyethylene (HDPE), and Polypropylene (PP), and that their thermal stability meets production requirements. Good compaction performance was observed with plastic content below 2% of the aggregate weight, while higher contents reduced void content due to the space occupied by plastics. When the plastic content increased from 0.5% to 2.0%, creep compliance decreased from 68.4% to 77.87%, while the m-value, tensile strength, and elastic energy maximum decreased by 30.77%, 5.6%, and 7%, respectively. In contrast, the failure strain, fracture energy, and maximum DSCE increased by 25.86%, 87.43%, and 133.05%, respectively. The recycled plastic enhanced the toughness of the asphalt mixture, increasing the dissipated energy during crack propagation and improving its resistance to permanent deformation. Moreover, the plastics hindered crack propagation through a bridging effect, leading to fewer cracks within plastic zones compared with surrounding areas. This study provides actionable guidance for the application of composite plastics in asphalt pavements and supports their sustainable development.