Experimental Investigation of Nanodiamond Reinforcement in PU for Enhancing Mechanical, Scratch, Rheological,...

Shape-memory polymers (SMPs) are a unique class of smart materials capable of recovering their original shape upon external stimuli, with thermoresponsive polyurethane (PU) being one of the most widely studied systems. However, the relatively low mechanical strength, thermal stability, and durability of PU limit its broader functional applications. PU/ND composites containing 0.1-0.5 wt.% ND were fabricated via melt blending and injection molding method. The objective was to evaluate the effect of ND reinforcement on the mechanical, scratch, thermal, rheological, and shape-memory properties. Results show that tensile strength increased up to 114% and Young's modulus by 11% at 0.5 wt.% ND, while elongation at break decreased due to restricted chain mobility. Hardness improved by 21%, and scratch resistance was significantly enhanced, with the coefficient of friction reduced by 56% at low loads. Thermal stability was improved, with the maximum degradation temperature shifting from 350 °C (pure PU) to 362 °C (0.5 wt.% PU/ND) and char yield increasing by 34%. DSC revealed an increase in glass transition temperature from 65 °C to 68.6 °C. Rheological analysis showed an 89% reduction in damping factor (tan δ), indicating enhanced elasticity. Shape-memory tests confirmed notable improvements in both shape fixity and recovery ratios across successive cycles compared to neat PU, with the highest enhancements observed for the 0.5 wt.% PU/ND nanocomposite-showing up to 7.6% higher fixity and 32% higher recovery than pure PU. These results demonstrate that ND reinforcement effectively strengthens PU while preserving and improving its shape-memory behavior, making the composites promising candidates for high-performance smart materials in sensors, actuators, and aerospace applications.