Highly Efficient Cellulose Nanofiber/Halloysite Nanotube Separators for Sodium-Ion Batteries

As a fundamental component of sodium-ion batteries, separators are considered to isolate two electrodes and simultaneously allow for the transport of ions. Cellulose separators have attracted widespread interest for their remarkable properties. In this study, we prepared composite separators comprising cellulose nanofibers (CNFs) and halloysite nanotubes (HNTs) for sodium-ion batteries. When the content of the HNT was up to 60%, the tensile strength and elongation at break of the composite separator (denoted as C/H-60) were 24.39 MPa and 2.22%, respectively. Importantly, the C/H-60 separator demonstrated a high porosity (69.08%), improved ionic conductivity (1.142 mS/cm), decent thermal stability, and good electrolyte retention (91.3% electrolyte uptake). The assembled sodium-ion battery containing the composite separators had an excellent rate capacity and cycling property. The proposed composite separators are expected to be applied in high-performance sodium-ion batteries.