Analysis of Microstructure and Pore Formation Mechanism in Magnetic Pulse-Assisted Semi-Solid Brazed Joints of Cu/Al...

In this study, the joining of Cu/Al tubes was achieved using the magnetic pulse-assisted semi-solid brazing (MPASSB) technique. A coupled finite element method-smoothed particle hydrodynamics (FEM-SPH) model was established to analyze the influence mechanism of solid-liquid interface interaction on pore formation during the brazing forming process. The results indicate that the MPASSB technique can produce Cu/Al tube joints with excellent metallurgical bonding and performance at 390 °C, and no brittle Cu/Al intermetallic compounds (IMCs) are formed in the joints. Additionally, a stronger solid-liquid interface interaction and a higher surface roughness of the tubes lead to easier peeling of the copper matrix from the interface, thereby promoting pore formation. Mechanical property tests show that the shear strength of the joints prepared by this method can reach 63.3 MPa, and the fracture occurs in the brazing seam area adjacent to the copper-side interface. The MPASSB technique is expected to provide a feasible technical approach for the high-quality joining of dissimilar Cu/Al materials.