The Effect of In Situ Heat Treatment on the Microstructure and Mechanical Properties of H13 Tool Steel Specimens...

Samples of H13 tool steel were produced using the LENS^® laser additive manufacturing technique. Three variants of samples were produced such that during and 2 h after deposition, both the substrate and sample temperatures were maintained at 80, 180, and 350 °C. After the samples were produced, the effect of the substrate temperature on their metallurgical quality, microstructure, and mechanical properties was determined. No segregation of alloying elements was observed. The test results indicate that, depending on the temperature used, the structure of the H13 alloy is martensitic or martensitic-bainitic with a slight residual austenite content of up to 2.1%. Owing to structural changes, the obtained alloy is characterized by lower impact strength compared with conventionally produced alloys and high brittleness, particularly when using an annealing temperature of 350 °C. Isothermal annealing above the martensite start temperature results in extreme brittleness due to a partial structural transformation of martensite into bainite and probable carbide precipitation processes at the nanoscale.