Technetium Immobilization on Carbon Steel Corrosion Products Under Simulated Geological Radioactive Waste Repository...

The migration of the long-lived isotope technetium-99 (half-life 2.1 × 10⁵ years) presents a significant challenge for the deep geological disposal of radioactive waste. This study investigates the immobilization of technetium by carbon steel corrosion products under aerobic and anaerobic conditions simulating the Yeniseysky site (Krasnoyarsk Region, Russia), a proposed location for a Deep Geological Repository (DGR). Over time, the degradation of barrier materials is expected to allow low-salinity solutions to be brought into contact St3 steel, the intended container material for vitrified radioactive waste in the Russian context, leading to crevice corrosion. The findings demonstrate that carbon steel containers act not merely as a physical barrier but also as a chemical barrier by facilitating the reductive immobilization of technetium. The most effective reduction of technetium was observed in the presence of ferrihydrite as a corrosion product under both aerobic and anaerobic conditions, as indicated by distribution coefficient (K_d) values ranging from 1.4 × 10³ to 1.6 × 10³ cm³/g. However, the presence of bentonite clay can diminish the efficiency of this process by adsorbing corrosion products, resulting in a 50% reduction in the distribution coefficients. In contrast, leaching products from aluminophosphate glass and cement had a less pronounced effect on technetium immobilization, causing a decrease in distribution coefficients of no more than 30%. The results of this research can be applied to model the long-term behavior of technetium in the evolving environment of a geological radioactive waste repository.