Study of Preparation and Performance Porous Thermal Insulation Refractory Materials from Aluminum Ash and Red Mud

The risk of environmental accumulation of aluminum ash and red mud is increasing, emphasizing the demand for high-value utilization. In this study, the conversion of aluminum ash and red mud into porous refractory materials with good thermal insulation performance is successfully demonstrated, demonstrating that both residues can be recovered as a resource and their environmental impact can be reduced in a sustainable manner. The phase composition and microstructure of the waste are evaluated by XRD and SEM/EDS, respectively, while their high-temperature behavior and performance were assessed through visual high-temperature furnace testing. The influence of the aluminum ash-red mud ratio on the rheological behavior of slurries containing surfactants at a constant alkaline pH was highlighted. A slurry composition of 40% red mud and 30% aluminum ash exhibited the lowest shear stress and viscosity values, required to facilitate bubble growth. Building on this formulation, foaming with 2% (mass fraction) H₂O₂ at 80 °C and sintering at 1250 °C produces a material with the optimum performance: a compressive strength of 1.03 MPa, a porosity of 58.55%, and thermal conductivity of 0.19 W/(m·K). The material exhibits long-lasting stability at temperatures ≤ 1100 °C. Thus, complementary compositions of aluminum ash and red mud show potential for practical application and value addition in the preparation of porous refractory materials with thermal insulation properties.