Preparation and Paclitaxel-Loading of Regenerated Chitin Nanoparticles

This study aims to investigate biodegradable and biocompatible chitin as a natural carrier for loading the hydrophobic anti-cancer drug paclitaxel (PTX) for the first time, resulting in a new loading system of chitin nanoparticles-paclitaxel (ChNps-PTX). The well-dispersed chitin nanoparticles (ChNps) and ChNps-PTX were prepared via a water-dripping regeneration method. The functional groups, crystal form, and the high degree of acetylation (DA = 96.03%) of ChNps did not change during regeneration, suggesting that ChNps retained the complete molecular structure of chitin. The average particle size of ChNps-PTX was approximately 93.11 nm, which was larger than that of ChNps (84.06 nm) because of loading PTX (the drug loading was approximately 8.01%). TEM and CLSM were employed to confirm PTX existence in ChNps-PTX, and the nano-strip PTX (30.52 ± 6.78 nm in length and 16.02 ± 2.77 nm in width) was found for the first time. Loading of PTX resulted in ChNps-PTX presenting a new characteristic peak at 1734 cm^-1 in FT-IR spectra, a new peak at 2θ = 5.3° in XRD pattern, and a new exothermic peak (252 °C) in DSC curve. While ChNps-PTX showed a lower crystallinity (19.86%) compared with that of ChNps (24.11%) and chitin (36.77%), utilizing the chitin carrier and mild regeneration method to load PTX were highly beneficial for pharmaceutical fields.