Mechanical Enhancement of Polychloroprene Adhesives via Reinforcement with Aluminum Oxide Nanofibers

In this study, we demonstrated chloroprene rubber (CR)-based composites with the addition of synthesized alumina nanofibers (AONF) with a high aspect ratio (>1000). AONF were characterized using transmission electron microscopy (TEM), scanning electron microscopy (SEM), and X-ray diffraction (XRD). AONF were introduced by pre-dispersion. The resulting chloroprene rubber/aluminum oxide nanofiber (CR/AONF) composites were subjected to tensile and shear adhesive bonding tests. The tensile test results for the CR/AONF composites are 81% greater than those of the original CR composite (0.85 MPa and 1.54 MPa, respectively). Shear adhesive bonding tests were conducted for glass and steel. CR/AONF demonstrates a 213% (for steel) and 262% (for glass) increase in shear strength. The main strengthening mechanisms are reinforcement, CR adsorption on the AONF surface, and crack arrest. These results may expand our understanding of the potential of sealant strengthening using AONF.