Influence of Nesquehonite on the Early-Stage Hydration of Portland Cement

Addressing the significant pressure for carbon emission reduction in the cement industry, the development of novel cement materials capable of achieving "in situ carbon sequestration" has become an important research focus. This study introduces nesquehonite (MgCO₃·3H₂O, NQ) as a functional admixture into the Portland cement system, systematically investigating its effects on the cement hydration process, the evolution of hydration products, and its carbon sequestration efficiency. Through designed penetration resistance tests and hydration tests with a high water-to-solid ratio, this research utilized X-ray diffraction analysis to determine the phase composition and content of hydration products at different ages. This was combined with scanning electron microscopy to observe microstructural evolution and Nano Measure software 1.2.5 for ettringite crystal size measurement, analyzing the impact of NQ on the early hydration process of P.I cement. The results indicate that the incorporation of NQ significantly alters the early hydration of P.I cement. The Mg²⁺ and CO₃^2- ions released upon its dissolution interact with Ca²⁺ and OH^- in the pore solution, effectively promoting the early precipitation of carbon sequestration products such as calcium carbonate and minor magnesium-containing carbonates. The addition of 10% NQ hindered the crystallization of Ca(OH)₂ before 6 h but promoted its formation after 24 h. Mechanical property tests revealed that a sample with an optimal 3% NQ dosage not only increased the paste's penetration resistance but also enhanced the compressive strength of the 1-day hardened sample by 8.37% compared to the plain sample, without a decrease and even a slight increase at 28 days. This enhancement is closely related to the microstructural strengthening effect induced by the carbonation products. This study confirms the feasibility of using NQ to steer the cement hydration pathway towards a low-carbon direction, revealing its dual functionality in regulating hydration and sequestering carbon within cement-based materials. The findings provide a new theoretical basis and technical pathway for developing high-performance, low-carbon cement.