High-Frequency Plasma Electrolytic Oxidation of an Al-Si Alloy: Influence of Al₂O₃ and SiO₂ Additives on Coating...

This study focuses on surface modification of aluminum alloys (Al-Si) with high silicon content using plasma electrolytic oxidation (PEO). The influence of Al₂O₃ and SiO₂ particles, introduced both separately and in combination, into a sodium aluminate-based electrolyte during high-frequency treatment (2000 Hz). Examination of surface and cross-sections using a scanning electron microscope SEM showed an increase in the compactness of the coating when Al₂O₃ particles were introduced. The addition of SiO₂ particles tended to promote a smoother surface and a slight reduction in the porosity and defect density. However, when these particles are added together, especially at high concentrations, an increase in structural defects and crack formation is observed. X-ray diffraction analysis revealed that the γ-Al₂O₃ phase was present in all coatings. In the samples with Al₂O₃ addition, the α-Al₂O₃ diffraction signal became stronger compared with the other coatings. Tribological tests revealed that the addition of Al₂O₃ particles significantly improved wear resistance, while the introduction of SiO₂ particles contributed to the stabilization of the friction coefficient. Thus, Al₂O₃ particles were the most effective in enhancing the mechanical properties of the coating.