A porous tellurium interlayer for high-power and long-cycling garnet-based quasi-solid-state lithium-metal batteries

Li-metal batteries with solid oxide electrolytes have garnered increasing attention as promising technologies that can overcome the safety and energy density limits of lithium-ion batteries (LIBs). However, the less than satisfactory long-term stability of Li-metal batteries-a consequence of Li dendrite formation caused by unstable Li plating/stripping at the interface between the Li metal and solid electrolyte-is hampering their commercialisation. Herein, we propose an negative electrode multilayer consisting of porous Te and carbon-based layers that can suppress Li dendrite formation and significantly lower the degree of capacity decay during long-term cycling. A quasi-all-solid-state Li-metal battery fabricated using Li_6.4La₃Zr_1.7Ta_0.3O₁₂ (LLZTO), a Te/Ag-C anodenegative electrode interlayer, and a LiNi_0.8Co_0.1Al_0.1O₂ (NCA811) positive electrode impregnated with an ion-conducting liquid demonstrated high capacity retention (80.1% over 4000 cycles) and Coulombic efficiency (99.7%) when operated at a high current density of 2.2 mA/cm² at 25 °C. Furthermore, we successfully demonstrate 100-mAh-level single cells in a pouch cell configuration using a large-area (36 cm²) LLZTO solid electrolyte and a 3.2-mAh/cm² LiCoO₂ (LCO) positive electrode capable of operating for >400 cycles at a 0.5 C-rate (85 mA/g).