Grain Size and Electrochemical Surface Modification Effects on Corrosion, Biological, and Technological Properties of...

Commercially pure (CP) titanium is widely used for long-term biomedical implants due to its high biocompatibility and corrosion resistance. However, its relatively low strength limits its use in highly loaded applications. Ultrafine-grained (UFG) titanium obtained through severe plastic deformation offers enhanced mechanical performance while maintaining the stability of CP titanium. This study investigates how electrochemical surface modification by anodization affects the corrosion, biological performance, and technological behavior of UFG titanium. TiO₂ layers with nanotubular and nanoporous morphologies were produced at anodization voltages between 20 and 60 V. Corrosion tests in physiological solution confirmed stable passive behavior with corrosion rates below 4 µm year^-1, and surface wettability increased markedly with anodization. Osteoblast-like MG-63 cells exhibited good viability on all anodized surfaces, with improved adhesion and proliferation on samples anodized at 60 V. The porous TiO₂ layers were successfully intercalated with dimethyl sulfoxide and ibuprofen, demonstrating potential for local drug delivery. Implantation simulations on real Nanoimplant^® prototypes confirmed sufficient mechanical stability of the anodized layer. Overall, the optimized anodization of UFG titanium enhances its biological response while maintaining corrosion resistance, supporting its clinical use in long-term dental and orthopedic implants with integrated drug-release functionality.