Silver Nanowire-Amorphous Indium Zinc Oxide Composite Electrodes for Transparent Film Heaters

Transparent conductive films based on silver nanowire meshes have demonstrated significant potential as alternatives to conventional tin-doped indium oxide and fluorine-doped tin oxide thin films. However, these materials feature high junction resistance, poor damp heat (DH) stability, and weak mechanical adhesion to substrates, which are critical issues that must be addressed before any practical applications. In this paper, transparent conducting films composed of silver nanowire (AgNW) frameworks and amorphous indium zinc oxide (IZO) fillers were prepared by a spin-coating method. The AgNW-IZO composite films exhibited a higher conductivity and better DH stability and adhesion to substrates than that of their constituent parts alone. The lowest sheet resistance of the composite films was 3.3 ohm/sq with approximately 70% transparency in the visible spectrum. No degradation was observed after 8 months. The excellent DH stability and mechanical adhesion might facilitate applications of these AgNW-IZO composite films in optoelectronic devices. Furthermore, the composite electrode is shown to have potential as a transparent heater.