Mechanism-Informed Interfacial Chemistry and Structural Evolution of TiS₂ During Ca²⁺ Intercalation in Concentrated...

This study examines the interfacial and structural evolution of titanium disulfide (TiS₂) during Ca²⁺ intercalation/deintercalation in concentrated aqueous CaCl₂. Electrochemical measurements were combined with ex situ X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy to characterize the solvation structure, potential window, and reversibility in concentrated CaCl₂ electrolytes. Increasing the CaCl₂ concentration from 1.0 to 8.0 M was accompanied by reduced gas evolution and an expanded practical operating window. Stepwise analysis identified the potential range -1.00 to 0.10 V (vs. the saturated calomel electrode) as a practical window that minimized TiO₂/S₈ formation while preserving reversible Ca²⁺ intercalation. Ex situ XRD showed reversible (001) shifts, consistent with interlayer expansion and contraction, and peak broadening was indicative of partial amorphization and defects. XPS revealed CaS and polysulfides (S_z^2-, 2 ≤ z ≤ 8) to be the prevalent surface species with limited Ca(OH)₂ and CaSO₄; within the detection limits, no chlorine-containing reduction products were observed after charging. The electrochemical and spectroscopic results indicate that intercalation is accompanied by partial sulfur-centered reduction and defect signatures, with associated changes in the interfacial charge-transfer characteristics and reversibility. These findings link the potential, interfacial chemistry, and lattice response, and suggest design considerations for stable aqueous multivalent-ion storage.