Influence of Niobium Content on the Chemical Composition, Microstructure, and Microhardness of Hardfacing Coatings...

This study investigates the chemical composition, microstructural evolution, and mechanical behavior of hardfacing coatings produced by Shielded Metal Arc Welding (SMAW) using electrodes with varying niobium (Nb) contents (0%, 2%, 4%, 6%, and 8%), deposited at a constant current of 120 A and employing two- and three-layer configurations. Optical Emission Spectroscopy (OES) revealed a significant reduction in niobium transfer efficiency, with the Nb content in the coatings reaching up to 3.5 wt%, approximately 50% lower than in the electrodes. Chromium (Cr) content also decreased with increasing Nb additions due to the higher thermochemical affinity of niobium for oxygen, which promotes the formation of Nb oxides during welding. X-ray diffraction (XRD) analyses confirmed the presence of complex carbides, primarily NbC and M₇C₃-type Cr carbides, embedded in eutectic austenitic matrices. The incorporation of niobium promoted grain refinement and the precipitation of primary NbC carbides, particularly in multilayer coatings where dilution effects were reduced. Scanning Electron Microscopy (SEM) and Energy-Dispersive Spectroscopy (EDS) provided additional evidence, revealing an increased density of NbC particles and a concomitant reduction in CrC particle size with higher Nb contents. Microhardness testing showed a slight increase in hardness with increasing niobium, attributed to the higher intrinsic hardness and finer size of NbC particles. Overall, these findings highlight the role of niobium as an effective grain refiner and hard-phase promoter in SMAW-applied coatings, providing a foundation for optimizing wear-resistant overlays for demanding industrial environments.