Cyclic Superelasticity, Elastocaloric Effect, and Shape Memory Effect of Solution-Treated Ti₅₀Ni₄₁Cu₇Co₂ Alloy

In recent years, there has been an increasing interest in studying multi-component alloys. A bulk solution-treated Ti₅₀Ni₄₁Cu₇Co₂ SMA was prepared and investigated. The functional properties, including phase transformation temperature, shape memory effect, cyclic superelasticity, and elastocaloric response, were systematically evaluated. The alloy exhibited a M_s temperature of around 250 K, which is beneficial for applications at room temperature. Shape memory effect with a maximum recoverable strain of 6.21% was obtained under a biased stress of 300 MPa. The superelasticity rapidly became stable during the cyclic test, reducing irrecoverable strain from 2.8% to 0.01% by the 10th cycle. After 250th superelastic cycles, the alloy exhibited a stable recoverable strain of 1.3%, and a lower critical stress for transformation (270 MPa, down from 405 MPa). The elastocaloric cooling effect reached -4.9 K at the 50th cycle and stabilized at -4.3 K thereafter. With an increase in operating temperature, the elastocaloric effect diminished and disappeared above 383 K, and the SMA retained a notable recoverable strain of ~0.5% up to 443 K.